Siliconizing of Molybdenum Plate Using Si2Cl6
- Details
- Category: Molybdenum knowledge
- Published on 07 August 2013
- Hits: 385
Molybdenum plate was siliconized using Si2Cl6 as a silicon source, and the siliconizing conditions and some of its properties were examined.
The siliconizing of the molybdenum plate began by the deposition here and there of island-like MoSi2 deposits 4 to 6m thick in the initial stage (after 10 min induction time).
And then coalescence of the deposits proceeded to form a uniform MoSi2 layer all over the molybdenum plate after 30 min siliconizing time.
The weight decrease of the siliconized plate by anodic dissolution in 0.2 M sulphuric acid reduced exponentially with increasing thickness of the MOSi2 layer, and no weight decrease was observed at all above 16m thickness.
The sea water corrosion and sea sand abrasion resistivities of the siliconized molybdenum plate increased with increasing siliconizing temperature and Si2Cl6 flow rate.
More molybdenum product: http://www.molybdenum.com.cn
Tel: 0592-5129696 Fax：0592-5129797
E-mail:
This email address is being protected from spambots. You need JavaScript enabled to view it.
Tungsten Picture Center: http://picture.chinatungsten.com
Tungsten Video Center: http://v.chinatungsten.com
Tungsten News & Tungsten Prices, 3G Version: http://3g.chinatungsten.com
sales@chinatungsten.com